选择性激光烧结激光能量密度与温度补偿规律研究

作者：董星涛，阮耀波，卢德林 日期：2009-04-21/span> 浏览：3045 查看PDF文档

选择性激光烧结激光能量密度与温度补偿规律研究

董星涛，阮耀波，卢德林
（浙江工业大学 机电工程学院，浙江 杭州 310032）

摘要：选择性激光烧结（SLS）成型预热温度从成型缸中间到缸壁呈降低趋势,由于预热温度不均匀，导致SLS成型件密度不均匀。针对这一问题，通过增加激光能量密度对预热温度不足进行了补偿。通过试验建立了激光能量密度差ΔE与预热温差ΔT的经验公式，并比较了温度补偿前后烧结件的机械强度。实验结果表明，通过增加激光能量密度对预热温度不足进行补偿，提高了产品机械强度。
关键词：选择性激光烧结;能量密度；烧结密度；温度补偿
中图分类号：TB32文献标识码：A文章编号：1001-4551(2009)03-0066-03

Research of the relationship between laser power density and
temperature compensation in selective laser sintering
DONG Xing-tao, RUAN Yao-bo, LU De-lin
(College of Mechanical Engineering, Zhejiang University of Technology, Hangzhou 310032, China)
Abstract: Preheating temperature from the middle to verge of cylinder trend is decreasing during selective laser sintering. As preheating temperature not uniform, resulting in heterogeneous density of SLS part. Aiming at this problem, the laser power density was increased to compensate preheating temperature. Experience formula between difference in laser power density and difference in temperature was established. The result shows that the mechanical strength can be improved through increasing the laser power density to compensate preheating temperature.
Key words: selective laser sintering(SLS); power density; sinter density; temperature compensation
参考文献(References):
［1］刘伟军.快速成型技术及应用［M］.北京：机械工业出版社，2005.
［2］李湘生.激光选区烧结的若干关键技术研究［D］.武汉：华中科技大学材料科学与工程学院，2001.
［3］赵宝军.选择性激光烧结快速成形工艺建模与优化研究[D].北京：北京航空航天大学材料科学与工程学院，2002.
［4］王正伟.基于温度场的选区激光烧结成型工艺关键技术研究［D］.杭州：浙江工业大学机电工程学院,2008.
［5］陈鸿.基于选择性激光烧结快速成型系统及其关键技术研究［D］.北京：北京理工大学机电工程学院,2001.
［6］于千,白培康,王建宏.复合尼龙粉末激光烧结快速成型技术进展［J］.工程塑料应用,2005,33（5）:77-79.
［7］王金宝，朱善安，林峰.目标识别在微光水平尺光点精度检测中的应用[J].机电工程，2006，23（2）：46-48.