铸态铁素体球铁减速箱的铸造技术

作者：何合林1,2 日期：2008-12-26/span> 浏览：3034 查看PDF文档

铸态铁素体球铁减速箱的铸造技术

何合林1,2
（1.浙江省机械工业情报研究所，浙江 杭州 310009;2.杭州杭氧铸造有限公司，浙江 杭州 310004）

摘要：针对厚大断面铁素体球铁减速箱的铸造，采用了呋喃树脂造型工艺，根据“均衡凝固”和“有限补缩”理论，选择了工艺参数，确定了工艺方案，通过冷铁的设置来预防厚大部位的缩松和缩孔，在熔炼工艺上采用了“高温铁水，低温浇注”和倒包球化处理等手段以获得优良的铸件。实践证明，该技术具有广阔的应用前景。
关键词：铁素体球铁；减速箱；均衡凝固；有限补缩
中图分类号：TG24文献标识码：B文章编号：1001-4551(2008)11-0111-02

Casting technology of ascast ferrite ductile iron reduction gearbox
HE He-lin1,2
(1. Zhejiang Mechanical Industry Information Institute, Hangzhou 310009, China;
2. Hangzhou Hangyang Casting Co.Ltd., Hangzhou 310004, China)
Abstract: The furan resin modeling technology was adopted to cast heavy section ferrite ductile iron reduction gearbox. According to the proportional solidification and limited feeding theories, the technology parameters and the technology plan were set. Shrinkage porosity and cavity of thick large position were prevented by chilling. The excellent castings were produced by the process of “high temperature molten iron, lowtemperature casting” and inverted packet spheroidization in melting technology. The practice shows that the teachnology has a wide application prospect.
Key words: ferrite ductile iron; reduction gearbox; proportional solidification; limited feeding
参考文献(References):
［1］魏兵，袁森，张卫华.铸件均衡凝固技术及应用［M］.北京：机械工业出版社，1998.
［2］章舟.呋喃树脂砂铸造生产及应用实例［M］.北京：化学工业出版社，2008.
［3］中国机械工程学会铸造分会.铸造手册第5卷——铸造工艺:第2版［M］.北京：机械工业出版社，2002.
［4］中国机械工程学会铸造分会.铸造手册第1卷——铸铁:第2版［M］.北京：机械工业出版社，2002.
［5］吴海德.球墨铸铁［M］.北京:中国水利水电出版社,2006.
［6］贾利国.基于PLC的消失模铸造泡沫模样成形装置[J].机电工程，2005，22（10）：23-25.