刃口磨削裂纹产生机理分析

作者：童鲁海1，周赵凤2 日期：2008-08-14/span> 浏览：3634 查看PDF文档

刃口磨削裂纹产生机理分析

童鲁海1，周赵凤2
（1.杭州职业技术学院 化学工程系，浙江 杭州 310018； 2.浙江树人大学，浙江 杭州 310015）

摘要：民用刀剪在加工过程中，由于磨削等原因，容易产生裂纹，引起刀剪刃口卷裂或产生缺口。首先分析了国内刀剪与国外产品之间的差距，简要介绍了刀剪的制造工艺，接下来针对裂纹形成原因，对刀剪磨削过程中的受力情况进行了理论分析。最后，结合3Cr13不锈钢刀剪，给出了加工过程中相应的避免裂纹产生的防范措施和方法。
关键词：民用刀剪；磨削；裂纹；分析
中图分类号：TG702文献标识码：B文章编号：1001-4551(2008)07-0112-03

Mechanism analysis of cutting edge crack in grinding process
TONG Lu-hai1，ZHOU Zhao-feng2
(1.Department of Chemical Engineering, Hangzhou Professional Technical College, Hangzhou 310018, China;
2.Zhejiang Shuren University, Hangzhou 310015, China)
Abstract: In grinding process of civil cutter, crack is easy to happen by the reason of grinding, and it causes gap. The difference between domestic products and foreign ones was analyzed. Then its manufacturing technics were introduced. Based on the reasons of crack, mechanical analysis in grinding process was presented. Finally, preventive measures were given, aiming at 3Cr13 stainless steel kitchen knife.
Key words: civil cutter; grinding; crack; analysis
参考文献(Reference):
［1］谢汝深.浅析刀剪产品磨削工艺及设备的改进［J］.机电工程，2006，35（7）：104.
［2］KANAZAWA K. Tribology in cutting ability of knife［J］. Journal of Japanese Society of Tribologists, 2005,50(6):435-440.
［3］钱泳，戴起勋，陈康敏，等.新型热剪刀片喷焊层组织和性能研究［J］.热加工工艺，2005（6）：34-36.
［4］王建国，王贵，刘晓刚.热剪刃表面堆焊层显微组织和性能研究［J］.机械工程材料，1999，23（4）：46-48.
［5］张广宏.高精度圆盘滚剪刀制造工艺的改进［J］.工具技术，2002（8）：66.
［6］罗文宣，薛俊峰，薄海青，等.整体硬质合金刀具磨削裂纹的原因分析及其工艺改进［J］.工具技术，2006，40（6）：37-40.
［7］马素媛，徐建辉，王东林，等.磨削对不同温度回火钢铁材料微观结构的影响［J］.材料热处理学报，2005，26（2）：47-50.